Spring Steel Billet 60Si2Mn is a premium alloy steel renowned for its exceptional elasticity, high tensile strength, and superior fatigue resistance—making it the material of choice for manufacturing high-performance springs and elastic components. Compliant with industry standards, this billet is engineered to withstand repeated stress, deformation, and harsh operating conditions, ensuring long-term reliability in critical applications.

whatsapp

wechat

2010 ESTABLISHED

410 EMPLOYEE

363+CLIENTS

13000+ trade

Why Choose Baosteel®

Never stop the technological innovation,more than 50 patents, so that every piece of Products becomes the masterpiece.From consulting to after-sales support, theall-weather, all-process, all-round, whole-hearted service system will Escort for you.

 

Product details

This Spring Steel Billet 60Si2Mn is designed to provide outstanding elasticity, high tensile strength, and superior fatigue resistance, making it ideal for critical spring applications that require long-term reliability under repeated stress. The composition and heat treatment parameters can be adjusted to meet specific mechanical property requirements, ensuring optimal performance in various operating environments.

Parameter Value Remarks
Standard GB/T 1222-2016 Chinese standard for spring steels
Grade 60Si2Mn Alloy spring steel with high elasticity
Chemical Composition (wt%)
– Carbon (C) 0.56 – 0.64 Enhances hardness and strength
– Silicon (Si) 1.50 – 2.00 Improves elastic limit and tempering stability
– Manganese (Mn) 0.60 – 0.90 Promotes hardenability and strength
– Chromium (Cr) ≤0.35 Controlled impurity
– Nickel (Ni) ≤0.40 Controlled impurity
– Copper (Cu) ≤0.25 Controlled impurity
– Phosphorus (P) ≤0.030 Minimized to reduce brittleness
– Sulfur (S) ≤0.025 Minimized to prevent hot cracking
Mechanical Properties (after quenching and tempering)
– Tensile Strength (Rm) 1270 – 1700 MPa High strength for load-bearing springs
– Yield Strength (ReL) ≥1170 MPa Ensures excellent elastic recovery
– Elongation (A) ≥5% Adequate ductility for forming
– Reduction of Area (Z) ≥25% Indicates good toughness
– Hardness 45 – 50 HRC Optimal for spring applications
– Fatigue Limit ≥550 MPa Resists failure under repeated loading (10⁷ cycles)
Heat Treatment
– Quenching 850 – 870°C, oil-cooled Achieves martensitic structure
– Tempering 350 – 500°C Balances hardness and toughness
Delivery Condition Hot rolled, annealed, or quenched & tempered Customizable per order
Typical Applications Automobile suspension springs, railway buffer springs, industrial valve springs, clutch springs, shock absorber springs Ideal for high-stress, cyclic-loading compon